Copolymer compositions prepared from triazine derivatives of polycarbonates

ABSTRACT

Triazine compounds are prepared by the reaction of a bisphenol or a hydroxy-terminated polycarbonate with a chlorocyanurate containing epoxy and/or aromatic substituents. The compounds derived from bisphenols or protected bisphenols may be converted to polycarbonates, which form copolymers with other polymers containing acid or amine groups or derivatives thereof.

This invention relates to the preparation of copolymer compositions from reactively capped polycarbonates.

The superior physical properties of aromatic polycarbonates, such as high tensile and impact strength and good thermal stability, render them useful in a large number of application areas. However, polycarbonates are deficient in certain properties such as solvent resistance. Therefore, there is considerable activity in the development of blends of polycarbonates with other polymers which modify their properties. Illustrative polymers of this type are polyamides, linear polyesters and various other polymers containing amine or carboxylate groups.

The blends thus prepared are, however, often themselves deficient in properties due to the incompatibility or unfavorable morphology of the polymers comprising them. Thus, blends of polycarbonates and polyamides tend to delaminate severely. It is expected that the compatibility of such blends could be improved by incorporating therein, in various proportions, a copolymer of the blend constituents.

Polycarbonate-polyester blends are not incompatible in the same way as polycarbonate-polyamide blends; in fact, their compatibility is demonstrated by numerous commercially distributed blends of this type. Nevertheless, controlled formation of polycarbonate-polyester copolymer has the potential for improving the properties of such blends, particularly mechanical and barrier properties.

The formation of such copolymers requires the presence of functional groups on the polycarbonate which are capable of undergoing reaction with the other polymer. Thus, the functionalization of polycarbonates is a prime concern relative to the preparation of copolymers therefrom.

An illustrative method of functionalizing polycarbonates is disclosed in U.S. Pat. No. 4,732,934. In this method, a hydroxy-terminated polycarbonate is caused to react with a tricarboxylic acid derivative such as trimellitic anhydride acid chloride. Said method is, however, disadvantageous to a certain extent because it requires the use of special procedures to prepare a hydroxyterminated polycarbonate, followed by an additional reaction (usually in solution) with the tricarboxylic acid derivative to form the functionalized polycarbonate.

Interest continues, therefore, in simplifying the procedures for preparing functionalized polycarbonates. One possible expedient is the employment of a functionalized chain termination agent in the preparation of the polycarbonate. Relatively unreactive chain termination agents such as phenol and t-butylphenol are commonly employed. Also known by way of disclosure in U.S. Pat. No. 4,853,458 and German Offenlegungsschrift 3,445,108 is the use as a chain termination agent of a carboxylated phenol or a phenol containing an olefinic functional group.

The present invention provides a class of copolymer compositions prepared from reactively capped polycarbonates by means of addition or exchange reactions with carboxylate or amine groups in other polymers.

The invention includes copolymer-containing compositions prepared by the reaction of a first polymer containing acid or amine groups or functional derivatives thereof with a polycarbonate having end groups of the formula ##STR1## wherein: each of A¹ and A² is a divalent aromatic radical;

R¹ is an alkyl, cycloalkyl or aromatic radical or ##STR2## R² is an aromatic radical or a radical of formula II; and R³ is a divalent aliphatic, alicyclic, heterocyclic or unsubstituted or substituted aromatic hydrocarbon radical.

In formula I, A¹ and A² are usually identical although compositions in which they are different are also contemplated. Suitable A¹ and A² values include m-phenylene, p-phenylene, 4,4'-biphenylene, 4,4'-bi(3,5-dimethyl)phenylene, 2,2-bis(4-phenylene)propane and similar radicals such as those which correspond to the dihydroxy compounds disclosed by name or formula (generic or specific) in U.S. Pat. No. 4,217,438, the disclosure of which is incorporated by reference herein. Also included are radicals containing non-hydrocarbon moieties. These may be substituents such as chloro, nitro, alkoxy and the like, and also linking radicals such as thio, sulfoxy, sulfone, ester, amide, ether and carbonyl. Most often, however, all A¹ and A² radicals are hydrocarbon radicals.

The A¹ and A² radicals preferably have the formula

--A³ --Y--A⁴ -- (III)

wherein each of A³ and A⁴ is a monocyclic divalent aromatic radical and Y is a bridging radical in which one or two atoms separate A³ from A⁴. The free valence bonds in formula IV are usually in the meta or para positions of A³ and A⁴ in relation to Y.

In formula III, the A³ and A⁴ values may be unsubstituted phenylene or substituted derivatives thereof, illustrative substituents (one or more) being alkyl, alkenyl, halo (especially chloro and/or bromo), nitro, alkoxy and the like. Unsubstituted phenylene radicals are preferred. Both A³ and A⁴ are preferably p-phenylene, although both may be o- or m-phenylene or one o- or m-phenylene and the other p-phenylene.

The bridging radical, Y, is one in which one or two atoms, preferably one, separate A³ from A⁴. It is most often a hydrocarbon radical and particularly a saturated radical such as methylene, cyclohexylmethylene, 2-[2.2.1]-bicycloheptylmethylene, ethylene, isopropylidene, neopentylidene, cyclohexylidene, cyclopentadecylidene, cyclododecylidene or adamantylidene, especially a gemalkylene (alkylidene) radical. Also included, however, are unsaturated radicals and radicals which contain atoms other than carbon and hydrogen; for example, 2,2-dichloroethylidene, carbonyl, phthalidylidene, oxy, thio, sulfoxy and sulfone. For reasons of availability and particular suitability for the purposes of this invention, the preferred radical of formula III is the 2,2-bis(4-phenylene)propane radical, which is derived from bisphenol A and in which Y is isopropylidene and A³ and A⁴ are each p-phenylene.

The R¹ value in formula I may be an alkyl or cycloalkyl radical, typically lower alkyl (i.e., alkyl containing up to 7 carbon atoms) and especially primary or secondary lower alkyl. It may also be an aromatic radical, typically monocyclic and containing 6-10 carbon atoms and especially an aromatic hydrocarbon radical. Finally, the R¹ radical may have formula II, in which R³ may be aliphatic, alicyclic, aromatic (including aromatic radicals containing art-recognized substituents) or heterocyclic. It is usually lower alkylene and especially methylene.

The R² value may be an aromatic radical or may have formula II. Thus, it may have the aromatic or epoxide-containing structures previously defined for R¹.

Polycarbonates having end groups of formula I may be prepared in a number of ways. In the first place, they are capable of direct preparation by reaction of a compound of formula V hereinafter with a hydroxy-terminated polycarbonate. Hydroxy-terminated polycarbonates may in turn be prepared by known transesterification reactions, by chain cleavage of a higher molecular weight polycarbonate, or by phosgenation with the employment of a tetrahydropyranyl ether as a chain termination agent as disclosed in the aforementioned U.S. Pat. No. 4,736,013, followed by deprotection by a procedure similar to that discussed hereinabove.

In the second place, polycarbonates having the required end groups may be prepared by employing a compound of the formula ##STR3## as a chain termination agent in a conventional polycarbonate formation reaction. Compounds of formula IV, as well as polycarbonates having end groups of formula I, are disclosed and claimed in copending, commonly owned application Ser. No. 7-495068.

The compounds of formula I may be prepared by effecting reaction between a dihydroxy compound of the formula HO-A¹ -OH and a chlorotriazine of the formula ##STR4## wherein R¹ and R² are as previously defined. The chlorotriazines of formula V include epoxychlorotriazines, in which at least one and often both of R¹ and R² have formula II. Typical epoxychlorotriazines of formula V include 2-chloro-4,6-diglycidoxy-l,3,5-triazine (hereinafter "DGCC"), 2-chloro-4-methoxy-6-glycidoxy-1,3,5-triazine, 2-chloro-4-(n-butoxy)-6-glycidoxy-1,3,5-triazine (hereinafter "BGCC") and 2-chloro-4-(2,4,6-trimethylphenoxy)-6-glycidoxy-l,3,5-triazine (hereinafter "MGCC"). These compounds may also be named as though derived from cyanuric acid and designated diglycidyl chlorocyanurate, methyl glycidyl chlorocyanurate, n-butyl glycidyl chlorocyanurate and 2,4,6-trimethylphenyl glycidyl chlorocyanurate, respectively. They may be prepared, for example, by the reaction of 2,4,6-trichlorotriazine (cyanuric chloride) with glycidol or combinations thereof with n-butanol, methanol or mesitol, as disclosed in U.S. Pat. No. 4,895,945. Cyanuric chloride and n-butyl dichlorocyanurate are both commercially available.

The compounds of formula V also include arylchlorotriazines, in which at least one and often both of R¹ and R² are aromatic radicals. Substituted phenyl groups in which the substituents have several identical hydrogen atoms, such as t-butylphenyl and methoxyphenyl, have the advantage of affording products in which the proportion of capping may be determined by proton nuclear magnetic resonance, utilizing the protons on the t-butyl or methoxy group. On the other hand, electron-withdrawing substituents such as halo, carboxy, carbalkoxy, nitrile, nitro, acyl and aldehyde groups may promote displacement by amine groups in a polyamide by reason of the lower pKa of the conjugate acid of the displaced aryloxide anion.

Typical arylchlorotriazines include 2-chloro-4,6-diphenoxy-1,3,5-triazine, 2-chloro-4,6-di-(4-t-butylphenoxy)-1,3,5-triazine and 2-chloro-4,6-di-(4-methoxyphenoxy)-l,3,5-triazine. When named as though derived from cyanuric acid, these compounds are designated diphenyl chlorocyanurate, di-(4-t-butylphenyl) chlorocyanurate and di-(4-methoxyphenyl) chlorocyanurate, respectively. They may be similarly prepared by the reaction of 2,4,6-trichlorotriazine (cyanuric chloride) with the corresponding hydroxyaromatic compounds, or sequentially with hydroxyaromatic compounds and aliphatic or alicyclic alcohols.

The reaction between the chlorotriazine and the dihydroxy compound may be conducted at temperatures in the range of about 35°-75° C. An organic solvent, typically a chlorinated aliphatic hydrocarbon such as methylene chloride or chloroform, is typically employed, and a basic reagent such as an alkali metal hydroxide or an amine is preferably employed as a catalyst and/or hydrogen chloride scavenger. Preferably, an alkali metal hydroxide is added incrementally. There may also be employed a phase transfer catalyst; any of such catalysts which are stable and effective under the prevailing reaction conditions may be used. Those skilled in the art will be able to choose suitable phase transfer catalysts. Particularly preferred are the tetraalkylammonium chlorides wherein at least two alkyl groups per molecule, typically 2 or 3, contain about 5-20 carbon atoms. Triazine compounds of formula IV are preferably prepared using a large excess of dihydroxyaromatic compound, typically about a 300-800% molar excess.

Following completion of the reaction, it is frequently preferred to neutralize the mixture and convert salts of the hydroxyaromatic compounds to the free hydroxy species. This is often conveniently done by adding gaseous or solid carbon dioxide.

Compounds of formula IV are generally obtained in admixture with a large proportion of excess dihydroxyaromatic compound, by reason of the proportions of reagents used in their preparation. For use as chain termination agents in polycarbonate preparation, they need not be isolated but may be used in crude form. If isolation of such compounds, either from excess dihydroxyaromatic compound or from other materials present in a deprotection reaction, is desired, it may be accomplished by flash chromatography with mixtures of non-polar and relatively polar solvents, the polar solvent being employed in progressively greater proportions as the chromatography proceeds.

Reactions forming polycarbonates with end groups of formula I typically involve interfacial phosgenation or bischloroformate reaction, in a mixture of water and a substantially water-immiscible organic liquid such as methylene chloride, under alkaline conditions and most often in the presence of an amine such as triethylamine as catalyst. The compound of formula IV is incorporated in proportions to afford a polycarbonate product of the desired molecular weight. This reaction is so well known to those in the art that an extended discussion thereof is unnecessary.

The preparation of the compounds of formula IV and polycarbonates containing end groups of formula I are illustrated by the following examples. All percentages are by weight. Molecular weights herein were determined by gel permeation chromatography relative to polystyrene.

EXAMPLE 1

A solution of 43.70 grams (192 mmol.) of bisphenol A, 12.30 grams (38 mmol.) of MGCC and 750 ml. of methylene chloride was stirred as 3.40 grams (42.5 mmol.) of 50% aqueous sodium hydroxide solution was added over 1/2 hour. After sodium hydroxide addition was complete, the mixture was heated under reflux for 18 hours. It was then cooled to room temperature and neutralized to a pH of 7 by the addition of solid carbon dioxide. The neutralized mixture was filtered and the filtrate was dried over anhydrous magnesium sulfate, filtered and vacuum stripped to yield the impure mono(epoxytriazine) derivative of bisphenol A as a thick oil. The crude material was useful as a chain termination agent for polycarbonates; however, separation of the pure triazine compound was achieved by flash chromatography with mixtures of ethyl ether and pentane.

EXAMPLE 2

A mixture of 20.6 grams (50 mmol.) of 2-chloro-4,6-di-(t-butyl)phenoxytriazine, 57 grams (250 mmol.) of bisphenol A, 1 liter of methylene chloride and 13 grams of a 10% solution in toluene of a commercially available tetraalkylammonium chloride as a phase transfer catalyst was stirred at room temperature as 20 grams (50 mmol.) of 10% aqueous sodium hydroxide solution was added over 30 minutes. Stirring was continued for 3 hours, after which the organic layer was separated, washed twice with aqueous sodium chloride solution and dried over magnesium sulfate. Upon vacuum stripping of solvent, the desired crude monotriazine derivative of bisphenol A was obtained as a mixture comprising about 20% of said derivative, with the balance being bisphenol A.

EXAMPLE 3

A mixture of 19.09 grams (84 mmol.) of bisphenol A, 1.511 grams (2.94 mmol.) of the chromatographically purified product of Example 1, 85 mg. (7.6 mmol.) of triethylamine in the form of a 5% solution in methylene chloride, 57 ml. of methylene chloride and 50 ml. of deionized water was charged to a five-necked Morton flask fitted with a pH probe, reflux condenser, phosgene dip tube, mechanical stirrer and addition funnel. Phosgene was bubbled into the mixture at 610 mg. per minute for 17 minutes, to a total of 10.37 grams (104.7 mmol.), with addition of 50% aqueous sodium hydroxide solution to maintain the pH at about 11. A total of 17.5 ml. of sodium hydroxide solution was added. The mixture was diluted with 150 ml. of methylene chloride, washed once with 0.5% aqueous hydrochloric acid solution and three times with water, and precipitated by pouring into one liter of methanol in a blender. Upon filtration and vacuum drying at 80 C, the desired epoxytriazine-capped polycarbonate was obtained; it had a weight average molecular weight of 61,100 and a number average molecular weight of 20,400, and was shown by high field proton nuclear magnetic resonance spectroscopy to contain a substantial proportion of aryloxyglycidoxytriazine end groups.

EXAMPLE 4

The procedure of Example 3 was repeated, employing 21.485 grams (110 mmol.) of bisphenol A, 111 mg. (10 mmol.) of triethylamine, 75 ml. of methylene chloride, 65 ml. of water and 13.6 grams (137.4 mmol.) of phosgene added at 800 mg. per minute over 17 minutes, and substituting 5.839 grams of the product of Example 2 (3.85 mmol. of monotriazine derivative) for the product of Example 1. The resulting aryloxytriazine-capped polycarbonate had a weight average molecular weight of 45,500 and a number average molecular weight of 9,700. It was shown by high field proton nuclear magnetic resonance spectroscopy to contain a substantial proportion of diaryloxytriazine end groups.

EXAMPLE 5

A bisphenol A polycarbonate having a weight average molecular weight of about 188,000 was degraded by extrusion on a twin-screw extruder at 288° C., yielding a hydroxy-terminated polycarbonate having a molecular weight of about 74,500. A solution of 3 grams of the hydroxy-terminated polycarbonate, 100 mg. of DGCC and about 0.2 ml. of pyridine in 25 ml. of chloroform was heated under reflux for 30 minutes. The product was precipitated by pouring the solution into methanol in a blender and was filtered, washed with methanol and dried in a vacuum oven. It was shown by proton nuclear magnetic resonance spectroscopy to contain about 0.48% epoxytriazine moieties.

EXAMPLE 6

A hydroxy-terminated bisphenol A polycarbonate having an intrinsic viscosity (in chloroform at 25° C.) of 0.38 dl./g. was prepared by the reaction of bisphenol A with diphenyl carbonate. A mixture of 400 grams of the hydroxy-terminated polycarbonate, 12 grams of DGCC, 48 grams of a 10% solution in toluene of a methyltrialkylammonium chloride in which the alkyl groups contained 8-10 carbon atoms (a phase transfer catalyst) and 2500 ml. of methylene chloride was stirred vigorously at room temperature and 24 grams of a 10% aqueous sodium hydroxide solution was added dropwise, with stirring which was continued for 30 minutes after base addition was complete. The product was precipitated by pouring the solution into methanol in a blender and dried in a vacuum oven. It had an intrinsic viscosity of 0.21 and was shown by proton nuclear magnetic resonance spectroscopy to contain about 0.67% epoxytriazine moieties.

The first polymer used in forming the copolymer-containing compositions of this invention is a polymer which contains acid or amine groups or functional derivatives thereof. Such polymers include polyamides and polyesters as well as olefin polymers containing such groups.

Polyesters suitable for preparing the compositions of the invention generally comprise structural units of the formula ##STR5## wherein each R⁴ is independently a divalent aliphatic, alicyclic or aromatic hydrocarbon or polyoxyalkylene radical and A⁵ is a divalent aromatic radical. They include thermoplastic polyesters illustrated by poly(alkylene dicarboxylates), elastomeric polyesters, polyarylates, and polyester copolymers such as copolyestercarbonates. Because the principal reaction which occurs with the epoxy groups in the capped polycarbonate involves a carboxylic acid group of the polyester, it is highly preferred that said polyester have a relatively high carboxylic end group concentration. Concentrations in the range of about 5-250 microequivalents per gram are generally suitable, with 10-100 microequivalents per gram being preferable, 30-100 being more preferable and 40-80 being particularly desirable.

The polyester may include structural units of the formula ##STR6## wherein R⁴ is as previously defined, R⁵ is a polyoxyalkylene radical and A⁶ is a trivalent aromatic radical. The A⁵ radical in formula VI is most often p- or m-phenylene or a mixture thereof, and A⁶ in formula VII is usually derived from trimellitic acid and has the structure ##STR7##

The R⁴ radical may be, for example, a C₂₋₁₀ alkylene radical, a C₆₋₁₀ alicyclic radiCal, a C₆₋₂₀ aromatic radical or a polyoxyalkylene radical in which the alkylene groups contain about 2-6 and most often 4 carbon atoms. As previously noted, this class of polyesters includes the poly(alkylene terephthalates) and the polyarylates. Poly(alkylene terephthalates) are frequently preferred, with poly(ethylene terephthalate) and poly(butylene terephthalate) being most preferred.

The polyester generally has a number average molecular weight in the range of about 20,000-70,000, as determined by intrinsic viscosity (IV) at 30° C. in a mixture of 60% (by weight) phenol and 40% 1,1,2,2-tetrachloroethane.

Any polyamide made by any known method may be used in the preparation of the compositions of this invention. In many instances, polyamides in which the amine end group concentration is at least about 60 meq./g. are particularly useful, but the invention also contemplates the use of polyamides with lower amine end group concentrations or, in the case of epoxytriazine-terminated polycarbonates, with carboxylic acid end groups.

Suitable polyamides include those of the type prepared by the polymerization of a monoamino-monocarboxylic acid or a lactam thereof having at least 2 carbon atoms between the amino and carboxylic acid group, of substantially equimolar proportions of a diamine which contains at least 2 carbon atoms between the amino groups and a dicarboxylic acid, or of a monoaminocarboxylic acid or a lactam thereof as defined above together with substantially equimolar proportions of a diamine and a dicarboxylic acid. The dicarboxylic acid may be used in the form of a functional derivative thereof, for example, an ester or acid chloride.

Examples of the aforementioned monoaminomonocarboxylic acids or lactams thereof which are useful in preparing the polyamides include those compounds containing from 2 to 16 carbon atoms between the amino and carboxylic acid groups, said carbon atoms forming a ring with the --CO--NH-- group in the case of a lactam. As particular examples of aminocarboxylic acids and lactams there may be mentioned ε-aminocaproic acid, butyrolactam, pivalolactam, ε-caprolactam, capryllactam, enantholactam, undecanolactam, dodecanolactam and 3- and 4-aminobenzoic acids.

Diamines suitable for use in the preparation of the polyamides include the straight chain and branched chain alkyl, aryl and alkaryl diamines. Illustrative diamines are trimethylenediamine, tetramethylenediamine, pentamethylenediamine, octamethylenediamine, hexamethylenediamine (which is often preferred), trimethylhexamethylenediamine, m-phenylenediamine and m-xylylenediamine.

Suitable dicarboxylic acids include those which contain an aliphatic or aromatic group containing at least 2 carbon atoms separating the carboxy groups. The aliphatic acids are often preferred; they include sebacic acid, octadecanedioic acid, suberic acid, glutaric acid, pimelic acid and adipic acid.

Both crystalline and amorphous polyamides may be employed, with the crystalline species often being preferred by reason of their solvent resistance. Typical examples of the polyamides or nylons, as these are often called, include, for example, polyamide-6 (polycaprolactam), 66 (polyhexamethylene adipamide), 11, 12, 63, 64, 6/10 and 6/12 as well as polyamides from terephthalic acid and/or isophthalic acid and trimethylhexamethylenediamine; from adipic acid and m-xylylenediamines; from adipic acid, azelaic acid and 2,2-bis(p-aminophenyl)propane or 2,2-bis-(p-aminocyclohexyl)propane and from terephthalic acid and 4,4'-diaminodicyclohexylmethane. Mixtures and/or copolymers of two or more of the foregoing polyamides or prepolymers thereof, respectively, are also within the scope of the present invention. Preferred polyamides are polyamide-6, 66, 11 and 12, most preferably polyamide-66.

The olefin polymers (hereinafter sometimes designated "polyolefins") which may be used in the preparation of the compositions of this invention are homopolymers and copolymers of known aliphatic olefins including ethylene, propylene, 1-butene, 2-butene, 1-pentene, 2-pentene, 2-methyl-l-pentene, 3-methyl-l-pentene, 1-octene and 1-dodecene. The C₂₋₆ olefins are preferred, with ethylene and propylene being most preferred.

For the purposes of the invention, it is essential for the polyolefin to have groups capable of reactions involving the epoxy groups or phenoxy groups in the polycarbonate. Those skilled in the art will be familiar with suitable substituents; examples are carboxylic acid groups and anhydrides and acidic esters thereof, sulfonic acid groups and amine groups. Carboxylic acid groups are preferred by reason of their availability and the high stability of copolymers prepared therefrom.

The substituents may be incorporated in the polyolefin by employing suitable functional comonomers, such as acrylic acid, maleic anhydride or allylamine, in the formation thereof. They may also be provided by graft polymerization on an already prepared polyolefin, using the same monomers, or by other art-recognized means of functionalization.

Either solution or melt blending procedures may be employed for the preparation of the compositions of this invention. Typical reaction temperatures are in the range of about 175°-350° C. Thus, relatively high boiling solvents such as o-dichlorobenzene, 1,2,4-trichlorobenzene or 1,2,3,4-tetrachlorobenzene are preferred for solution reactions.

Melt reaction procedures are frequently preferred because of the availability of melt blending equipment in commercial polymer processing facilities. Conventional equipment of this type is suitable, with the use of extrusion equipment generally being convenient and therefore often preferred.

The compositions of this invention may also contain conventional ingredients such as fillers, flame retardants, pigments, dyes, stabilizers, anti-static agents, crystallization aids, mold release agents and the like. Resinous components not previously discussed, especially elastomeric impact modifiers, may also be present.

The preparation of the compositions of this invention is illustrated by the following examples.

EXAMPLES 7-13

Mixtures of 5 grams of the epoxytriazine-capped polycarbonate of Example 5, 5 grams of various carboxy-functionalized or anhydride-functionalized olefin polymers and 100 ml. of 1,2,3,4-tetrachlorobenzene were heated at 265° C. for 1 hour, with stirring. The mixtures were then cooled, precipitated by pouring into 1 liter of methanol in a blender and filtered. The filtration residues were reslurried three times with additional 1-liter portions of methanol, filtered after each operation and vacuum dried for 4 hours at 80° C.

About 10 grams of each dried product was accurately weighed and extracted in a Soxhlet extractor with 300 ml. of chloroform over 18 hours. The extraction residue and the residue obtained by evaporating the chloroform were dried and weighed and the percentage of copolymer formation determined therefrom. The results are given in the following table.

    ______________________________________                                                                        Copolymer,                                      Example                                                                               Olefin polymer          %                                               ______________________________________                                          7     Ethylene-acrylic acid (8%)                                                                             30                                               8     Propylene-acrylic acid (6%)                                                                            30                                               9     Propylene-maleic anhydride (0.5%),                                                                     40                                                     hydrolyzed                                                              10     Ethylene-maleic anhydride, hydrolyzed                                                                  10                                              11     Ethylene-maleic anhydride (1.25%)                                                                      10                                              12     Propylene-maleic anhydride (0.5%)                                                                      15                                              13     Propylene-styrene-maleic anhydride                                                                     25                                              ______________________________________                                    

EXAMPLE 14

A dry blend of 250 grams of the epoxytriazine-capped polycarbonate of Example 3 and 250 grams of a commercially available styrene-maleic anhydride copolymer containing 14% maleic anhydride was tumble mixed and extruded on a twin-screw extruder at temperatures in the range of 125°-265° C. The extrudate was quenched in water, pelletized and dried in an air-circulating oven for 4 hours at 100° C. After drying, it was extracted with ethyl acetate in a Soxhlet extractor. The weights of extracted material and residue showed the presence of 17% copolymer.

EXAMPLE 15

A mixture of equal weights of the aryloxytriazine-capped polycarbonate of Example 4 and a commercially available polyamide-6 was heated at 260° C. for about 8 minutes, with stirring. Upon cooling, Soxhlet extraction with chloroform and analysis, it was found that about 11% copolymer was present. 

What is claimed is:
 1. A copolymer-containing composition prepared by the reaction of a first polymer containing acid or amine groups or functional derivatives thereof with a polycarbonate having end groups of the formula ##STR8## wherein: each of A¹ and A² is a divalent aromatic radical;R¹ is an alkyl, cycloalkyl or aromatic radical or ##STR9## R² is an aromatic radical or a radical of formula II; and R³ is a divalent aliphatic, alicyclic, heterocyclic or unsubstituted or substituted aromatic hydrocarbon radical.
 2. A composition according to claim 1 wherein each of A¹ and A² has the formula--A³ --Y--A⁴ -- (III) wherein each of A³ and A⁴ is a monocyclic divalent aromatic radical and Y is a bridging radical in which one or two atoms separate A³ from A⁴.
 3. A composition according to claim 2 wherein each of A³ and A⁴ is p-phenylene and Y is isopropylidene.
 4. A composition according to claim 2 wherein at least one of R¹ and R² has formula II.
 5. A composition according to claim 4 wherein R³ is methylene.
 6. A composition according to claim 5 wherein one of R¹ and R² is a C₆₋₁₀ aromatic hydrocarbon radical.
 7. A composition according to claim 2 wherein each of R¹ and R² is a C₆₋₁₀ aromatic hydrocarbon radical.
 8. A composition according to claim 7 wherein the first polymer is a polyamide.
 9. A composition according to claim 7 wherein the first polymer is a polyester.
 10. A composition according to claim 7 wherein the first polymer is an olefin polymer containing acid or amine groups or functional derivatives thereof. 